1 苏州科技学院物理科学与技术系, 江苏 苏州 215009
2 中国科学院上海硅酸盐研究所 透明光功能无机材料重点实验室, 上海 201800
采用提拉法生长Nd掺杂原子数分数为1%的高质量的Nd:Lu3Al5O12(Nd:LuAG)晶体。对晶体的光谱性能进行了表征。研究发现,Nd:LuAG晶体与相同掺杂浓度的Nd:YAG晶体均具有相似的峰形和峰位,但特征吸收峰和荧光峰均发生了1 nm的红移现象。Nd:LuAG晶体具有比Nd:YAG和NdGGG晶体更长的荧光寿命和更宽的吸收线宽。在抽运功率为900 mW的钛宝石激光器抽运下,Nd:LuAG晶体获得了420 mW的连续激光输出,斜率效率为47.5%,激光抽运阈值为22 mW。
材料 Nd:LuAG晶体 吸收光谱 荧光光谱 激光性能
Author Affiliations
Abstract
We investigate the spectra and scintillation properties of Ce:YAlO3, Ce:Y3Al5O12, and Ce:LaAlO3. For Ce:YAlO3, the excitation spectrum is very similar with the absorption spectrum; for Ce:Y3Al5O12 and Ce:LaAlO3, the excitation spectra are different from the absorption spectra. Further, Ce:YAlO3 has better scintillation performance than Ce:Y3Al5O12; whereas Ce:LaAlO3 has not demonstrated scintillation performance to date. We also provide reasonable explanations for these experimental phenomena from the viewpoint of energy level structure.
160.4670 Optical materials 160.4760 Optical properties 160.5690 Rare-earth-doped materials Chinese Optics Letters
2012, 10(7): 071601
1 苏州科技学院 物理科学与技术系,江苏 苏州 215009
2 中国科学院 上海光学精密机械研究所,上海 201800
3 中国科学院 上海硅酸盐研究所,上海 201800
采用提拉法生长Yb3+掺杂原子数分数为10%高质量的Yb:Lu3Al5O12(Yb:LuAG)晶体。对晶体在不同气氛下退火的光谱性能进行了表征。研究发现,吸收光谱中363和562 nm附近的吸收带与Yb2+有关。晶体在空气气氛下退火后,测得的荧光光谱强度最强,荧光寿命最长。增益截面曲线的研究表明Yb:LuAG晶体具有宽的发射带。在抽运功率为9.59 W的激光二极管(LD)抽运下,Yb:LuAG晶体获得3.05 W的连续激光输出,斜率效率为41.7%,激光抽运阈值为40 mW。
材料 Yb:LuAG晶体 吸收光谱 荧光光谱 激光性能